Made for bonding and potting high-temperature sensors and heating elements, this air-setting cement powder is rated to 1425°C (2600°F). It is mixed with water to a smooth, uniform consistency and air-dries before heat curing. It develops a bond strength near 25.9 bar (375 psi). Works great for thermocouple cementing, element embedding, and refractory repair.
Made for bonding and potting high-temperature sensors and heating elements, this air-setting cement powder is rated to 1425°C (2600°F). It is mixed with water to a smooth, uniform consistency and air-dries before heat curing. It develops a bond strength near 25.9 bar (375 psi). Works great for thermocouple cementing, element embedding, and refractory repair.
Air Set Cements set or cure through loss of moisture by evaporation. Atmospheric conditions therefore affect the drying rate. Air Set Cements are used mainly in thin film applications (applied in thicknesses less than 1/4").
Features
Applications
| Packaging | 8 fluid oz |
| Type of cement (1 or 2 part) | 1 part |
| Coefficient of thermal expansion, in/in°F | 13.0 x 10-6 |
| Color | Tan to gray |
| Compressive strength, psi | 3300 |
| Dielectric constant | 3.4 to 4.5 |
| Dielectric strength at 20°C (70°F), V/mil | 12.5 to 51.0 |
| Dielectric strength at 400°C (750°F), V/mil | ≤15.0 |
| Dielectric strength at 795°C (1475°F), V/mil | ≤1.3 |
| Maximum service temperature | 2600°F (1425°C) |
| Shear strength, psi | 375 |
| Tensile strength, psi | 325 |
| Volume resistivity at 20°C (70°F), Ω-cm | 10 8-109 |
| Volume resistivity at 400°C (750°F), Ω-cm | 10 5-106 |
| Volume resistivity at 795°C (1475°F), Ω-cm | 10 3-104 |
| Thermal conductivity, btu-in/ft2-hr-°F | 11 |
| Mix ratio | 1-part cement; just mix powder with water to a smooth, uniform consistency |
| Packaging | 8 fluid oz |
| Type of cement (1 or 2 part) | 1 part |
| Coefficient of thermal expansion, in/in°F | 13.0 x 10-6 |
| Color | Tan to gray |
| Compressive strength, psi | 3300 |
| Dielectric constant | 3.4 to 4.5 |
| Dielectric strength at 20°C (70°F), V/mil | 12.5 to 51.0 |
| Dielectric strength at 400°C (750°F), V/mil | ≤15.0 |
| Dielectric strength at 795°C (1475°F), V/mil | ≤1.3 |
| Maximum service temperature | 2600°F (1425°C) |
| Shear strength, psi | 375 |
| Tensile strength, psi | 325 |
| Volume resistivity at 20°C (70°F), Ω-cm | 10 8-109 |
| Volume resistivity at 400°C (750°F), Ω-cm | 10 5-106 |
| Volume resistivity at 795°C (1475°F), Ω-cm | 10 3-104 |
| Thermal conductivity, btu-in/ft2-hr-°F | 11 |
| Mix ratio | 1-part cement; just mix powder with water to a smooth, uniform consistency |