Made for bonding and potting high-temperature sensors and heating elements, this air-setting cement liquid is rated to 1205°C (2200°F). It mixes with the matching powder at 2 to 1 by weight to form a ceramic bond. Works great for thermocouple cementing, heating-element embedding, and refractory repair.
Made for bonding and potting high-temperature sensors and heating elements, this air-setting cement liquid is rated to 1205°C (2200°F). It mixes with the matching powder at 2 to 1 by weight to form a ceramic bond. Works great for thermocouple cementing, heating-element embedding, and refractory repair.
Air Set Cements set or cure through loss of moisture by evaporation. Atmospheric conditions therefore affect the drying rate. Air Set Cements are used mainly in thin film applications (applied in thicknesses less than 1/4").
Features
Applications
| Packaging | 8 fluid oz |
| Type of cement (1 or 2 part) | 2 part |
| Coefficient of thermal expansion, in/in°F | 10.93 x 10-6 |
| Color | Off white |
| Compressive strength, psi | 1500 |
| Maximum service temperature | 2200°F (1205°C) |
| Tensile strength, psi | 1500 |
| Density (wet), lbs/ft3 | 112 |
| Density (dry), lbs/ft3 | 82 |
| Flexural strength, psi | 2000 |
| Modulus of elasticity, psi | 3.6 x 105 |
| Pot life, hr | 1.0 |
| Mix ratio | 2-part cement: just mix powder and binder; mix ratio for cast applications ranges from 1.87 to 2.0 parts powder to 1-part liquid binder by weight |
| Packaging | 8 fluid oz |
| Type of cement (1 or 2 part) | 2 part |
| Coefficient of thermal expansion, in/in°F | 10.93 x 10-6 |
| Color | Off white |
| Compressive strength, psi | 1500 |
| Maximum service temperature | 2200°F (1205°C) |
| Tensile strength, psi | 1500 |
| Density (wet), lbs/ft3 | 112 |
| Density (dry), lbs/ft3 | 82 |
| Flexural strength, psi | 2000 |
| Modulus of elasticity, psi | 3.6 x 105 |
| Pot life, hr | 1.0 |
| Mix ratio | 2-part cement: just mix powder and binder; mix ratio for cast applications ranges from 1.87 to 2.0 parts powder to 1-part liquid binder by weight |